LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding,PA6+GF30%, General PurposeApplication: Automotive (Cooling Fan)CAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 162 MPa @Thickness 3.20 mm |
23500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 4.5 % @Thickness 3.20 mm |
4.5 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 255 MPa @Thickness 6.40 mm |
37000 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 8.83 GPa @Thickness 6.40 mm |
1280 ksi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.39 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.00 mm |
508 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 260 - 285 °C | 500 - 545 °F | Injection Molding |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Nozzle Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 1067 Splicing Compound Kit
- Permabond MM115 Anaerobic Threadlocker
- Hybrid Plastics MS0825 Nanoreinforced® POSS® Polyamide 6
- Malvern Minerals Trikup® PT Silane Treated Aluminum Hydroxide
- Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
- SYNTHOS Koplen® 0207 FR Expandable Polystyrene
- Teknor Apex Telcar® OBC 4965A Thermoplastic Elastomer
- Unitika AX-1500 Dry
- Esstech X-768-0000 1,3-Glycerol Dimethacrylate, C11H16O5
- Eurotec® Tecomid® NB40 KG30 NL 0G PA6, 30% glass fiber/glass bead reinforced, natural
Copyright © lookpolymers.com All Rights Reserved