LG Chemical LUMAX GN5006FC PBT+ABS, Heat Resistance

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Heat Resistant
Manufacturer LG Chemical
Trade Name LUMAX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMAX GN5006FC PBT+ABS, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+ABS, Halogen Free Flame RetardantApplication: E&E (Connector)CAS: 9003-56-9, 9003-54-7 and 24968-12-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 47.1 MPa

@Thickness 3.20 mm
 6830 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 13 %

@Thickness 3.20 mm
 13 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 70.6 MPa

@Thickness 3.20 mm
 10200 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 2.26 GPa

@Thickness 3.20 mm
 327 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 1.47 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.76 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
Peak at Break
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 6.40 mm
 176 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.20 mm
 140 °F

@Thickness >=0.0472 in
60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
Flammability, UL94 V-2

@Thickness >=1.20 mm
 V-2

@Thickness >=0.0472 in
V-2

@Thickness >=1.50 mm
 V-2

@Thickness >=0.0591 in
V-2

@Thickness >=3.00 mm
 V-2

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 230 °C
428 - 446 °F
Injection Molding
Middle Barrel Temperature 225 - 235 °C
437 - 455 °F
Injection Molding
Front Barrel Temperature 225 - 235 °C
437 - 455 °F
Injection Molding
Nozzle Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Melt Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding