Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

DSM Akulon® K225-KV PA6 FR(30)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® K225-KV PA6 FR(30).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame Retardant (Halogen free), Heat stabilized
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
dry; ISO 1183
Water Absorption 7.5 %
7.5 %
Sim. To ISO 62
Moisture Absorption 2.00 %
2.00 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
cond; ISO 527-1/-2
70.0 MPa
10200 psi
dry; ISO 527-1/-2
Elongation at Break 4.0 %
4.0 %
dry; ISO 527-1/-2
>= 50 %
>= 50 %
cond; ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
dry; ISO 527-1/-2
30 %
30 %
cond; ISO 527-1/-2
Tensile Modulus 1.60 GPa
232 ksi
cond; ISO 527-1/-2
4.20 GPa
609 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 dry; ISO 179/1eA
0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 cond; ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min; ISO 11357-1/-3
Flammability, UL94 V-2

@Thickness 0.380 mm
 V-2

@Thickness 0.0150 in
 ,dry; IEC 60695-11-10
V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
 ,dry; IEC 60695-11-10
Glow Wire Test 850 °C

@Thickness 3.00 mm
 1560 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature, dry; IEC 60695-2-13
930 °C

@Thickness 0.380 mm
 1710 °F

@Thickness 0.0150 in
 Glow Wire Ignition Temperature, dry; IEC 60695-2-13
960 °C

@Thickness 0.380 mm
 1760 °F

@Thickness 0.0150 in
 Glow Wire Flammability Index, dry; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Glow Wire Flammability Index, dry; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
cond; IEC 60093
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
dry; IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
cond; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 dry; IEC 60250
3.3

@Frequency 100 Hz
 3.3

@Frequency 100 Hz
 dry; IEC 60250
3.6

@Frequency 1.00e+6 Hz
 3.6

@Frequency 1.00e+6 Hz
 cond; IEC 60250
8.0

@Frequency 100 Hz
 8.0

@Frequency 100 Hz
 cond; IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
cond; IEC 60243-1
30.0 kV/mm
762 kV/in
dry; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
 0.0090

@Frequency 100 Hz
 dry; IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 dry; IEC 60250
0.080

@Frequency 1.00e+6 Hz
 0.080

@Frequency 1.00e+6 Hz
 cond; IEC 60250
0.125

@Frequency 100 Hz
 0.125

@Frequency 100 Hz
 cond; IEC 60250
Comparative Tracking Index 600 V
600 V
dry; IEC 60112