SABIC Innovative Plastics Noryl TN240 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl TN240 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. Unfilled. Transparent. Good flow. Scratch resistant. Injection molding. Suitable for housewares, personal care and small appliance applications.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D 785 |
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 10 % | 10 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 3.4 % | 3.4 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 3.15 GPa | 457 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.82 GPa | 409 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.260 J/cm @Temperature 23.0 °C |
0.487 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.40 J/cm @Temperature 23.0 °C |
4.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.588 | 1.588 | ASTM D 542 |
| Haze | 6.6 % @Thickness 2.54 mm |
6.6 % @Thickness 0.100 in |
ASTM D 1003 |
| Transmission, Visible | 83.9 % @Thickness 2.54 mm |
83.9 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- Quadrant Plastic Composites MultiQ® Concrete Thermoplastic Panel Composite
- Kolon KOCETAL® GF105 G/F Reinforced Acetal Resin
- Solvay Chemicals CASO® Granular Anhydrous Calcium Chloride
- Goodfellow Ni-Mn-Ga Magnetic Shape Memory Alloy (MSM)
- A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene
- Ashley Polymers Ashlene® C1174,C1175 Polycarbonate
- Axiall 12770 Coax & Telecom Flexible PVC
- Kleerdex Kydex® 200 Acrylic/PVC Thermoplastic Sheet (discontinued **)
Copyright © lookpolymers.com All Rights Reserved