- Sichuan Deyang Haton® hGR20 Polyphenylene Sulfide, Glass Fiber Reinforced
Sichuan Deyang Haton® hGR20 Polyphenylene Sulfide, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR20 Polyphenylene Sulfide, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 102 | 102 | GB/T 3398.2-2008 |
| Tensile Strength | 130 MPa | 18900 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.8 % | 1.8 % | GB/T1040.2-2006 |
| Flexural Strength | 190 MPa | 27600 psi | GB/T 9341-2008 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 9.60 kJ/m² | 4.57 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.20e+16 ohm-cm | 2.20e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 9.80e+15 ohm | 9.80e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 3.2 | 3.2 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- MV Labs LA300 La2(CO3)3·xH2O Lanthanum carbonate hydrate
- Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound
- PolyOne Bergamid™ B70 VN4805 LS PM-Z BK Polyamide 6 (Nylon 6)
- SABIC Innovative Plastics Cycoloy® FXC810SL PC+ABS (Europe-Africa-Middle East)
- Fainplast Compounds RK 325 Rigid PVC, Extrusion Lead Free
- Momentive Performance Materials TUFELâ„¢ II 94706 Low Volatile Extrusion Heat Cured Rubber
- SABIC Innovative Plastics ULTEM 1285 PEI (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon
- BorsodChem ONGROVIL S-465 Suspension PVC-Resin
- Phenolic 30%, Graphite fabric 70%
Copyright © lookpolymers.com All Rights Reserved