Covestro Makrolon® DP 1-1265 Polycarbonate, Injection Grade  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® DP 1-1265 Polycarbonate, Injection Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding grade with exceptionally good flow, for Digital Versatile Discs (DVD).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Water Absorption 0.35 %
0.35 %
Saturation in water
Moisture Absorption at Equilibrium 0.15 %
0.15 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.35 %
0.35 %
Melt Flow 71 g/10 min

@Load 1.20 kg,
Temperature 300 °C
71 g/10 min

@Load 2.65 lb,
Temperature 572 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
Elongation at Break 50 %
50 %
Nominal
Elongation at Yield 6.0 %
6.0 %
Tensile Modulus 2.30 GPa
334 ksi
Charpy Impact Unnotched NB
NB
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Vicat Softening Point 142 °C
288 °F
Glass Transition Temp, Tg 143 °C
289 °F
Optical Properties Metric English Comments
Refractive Index 1.583
1.583
DIN 5026-1
Transmission, Visible >= 89 %

@Thickness 1.00 mm
>= 89 %

@Thickness 0.0394 in
ISO 489-A