LG Chemical LUCEL HI510 POM+Rubber, High Impact
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | LG Chemical |
| Trade Name | LUCEL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCEL HI510 POM+Rubber, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, POM+Rubber, High ImpactApplication: Gears, Automobile ClipCAS No. 66455-31-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.017 - 0.020 cm/cm @Thickness 3.20 mm |
0.017 - 0.020 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 190 °C |
14 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 90 % @Thickness 3.20 mm |
90 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 64.7 MPa @Thickness 3.20 mm |
9390 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.20 mm |
270 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
2.20 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness 0.950 - 2.90 mm |
122 °F @Thickness 0.0374 - 0.114 in |
|
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 0.950 - 2.90 mm |
122 °F @Thickness 0.0374 - 0.114 in |
|
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 0.950 - 2.90 mm |
122 °F @Thickness 0.0374 - 0.114 in |
|
| Flammability, UL94 | HB @Thickness >=0.980 mm |
HB @Thickness >=0.0386 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding |
| Back Pressure | 0.490 - 3.04 MPa | 71.1 - 441 psi | Injection Molding |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 5585 Carboxylated Styrene - Butadiene Copolymer
- Polymer Resources PEI-G40 Polyetherimide, 40% Glass Reinforced
- SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific)
- Styron CALIBREâ„¢ 302-6 Polycarbonate Resin
- DuPont Performance Polymers Zytel® RS LC1600 BK385 Nylon 1010 (Unverified Data**)
- Fainplast Compounds PM 9012 Flexible PVC, Extrusion
- Braskem FL31 LLDPE Cast Film Extrusion Polyethylene Copolymer
- Solvay RHODAFAC® RS-610 Surfactant
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
- Huntsman AVALON® 85 ABU Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved