SABIC Innovative Plastics LNP THERMOCOMP RF003AXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF003AXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF003AXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this material includes: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.740 % | 0.740 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 107 MPa | 15500 psi | 5 mm/min; ISO 527 |
| 109 MPa | 15800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.14 GPa | 891 ksi | 5 mm/min; ASTM D638 |
| 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.05 GPa | 732 ksi | 2 mm/min; ISO 178 |
| 5.47 GPa | 793 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.81 J/cm | 7.14 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products HP513-01 High Stiffness Polypropylene Copolymer, Medium Impact, UV Stabilized, Black
- Nilit FRIANYL B63 F Raw extruded nylon 6 for injection molding
- SABIC Innovative Plastics Lexan® LUX9612G PC (Asia Pacific)
- SABIC Innovative Plastics Lexan® XHT1141 PC
- Pau Tai UNINOX AM-929 Acrylic Impact Modifier
- Ferro IP 780 Passivation Glasses (Pb-B-Si-Al; Pb-Si-Al; Si-Pb-Al Silicates)
- Kolon SPESIN® KP212G30V0HI G/F Reinforced & Flame Retardant PBT Compound Resin
- Silberline Tufflake® 3720
- Dow C7014-35RNA Polypropylene Impact Copolymer Resin
- C.O.I.M. LARIPUR® LPR6325 Special Adipate Ester Polyurethane
Copyright © lookpolymers.com All Rights Reserved