LG Chemical HIPS 406AF PS, Flame Retardant

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant
Manufacturer LG Chemical
Trade Name HIPS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical HIPS 406AF PS, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PS, Flame RetardantApplication: Office Appliances (Parts of Printer or Copier)CAS: 9003-55-8, 25713-60-4 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 11 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 103
103
ASTM D785
Tensile Strength, Yield 32.4 MPa

@Thickness 3.20 mm
 4690 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 50 %

@Thickness 3.20 mm
 50 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 52.0 MPa

@Thickness 3.20 mm
 7540 psi

@Thickness 0.126 in
 15mm/min; ASTM D790
Flexural Modulus 2.45 GPa

@Thickness 3.20 mm
 356 ksi

@Thickness 0.126 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.392 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 0.735 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
0.392 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 0.735 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.490 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 0.918 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
0.785 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.47 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C

@Thickness 6.40 mm
 185 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C

@Thickness 6.40 mm
 174 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 85.0 °C

@Load 5.00 kg
 185 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=2.50 mm
 122 °F

@Thickness >=0.0984 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=2.50 mm
 122 °F

@Thickness >=0.0984 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=2.50 mm
 122 °F

@Thickness >=0.0984 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
Flammability, UL94 V-2

@Thickness >=1.50 mm
 V-2

@Thickness >=0.0591 in
V-2

@Thickness >=2.50 mm
 V-2

@Thickness >=0.0984 in
V-2

@Thickness >=3.00 mm
 V-2

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 200 °C
374 - 392 °F
Injection Molding
Front Barrel Temperature 200 - 210 °C
392 - 410 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 60.0 - 70.0 °C
140 - 158 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding