LATI Latistat 73/13-06 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	LATI
Trade Name	Latistat
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latistat 73/13-06 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Dissipative product based on Polyoxymethylene (POM). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.40 g/cc	0.0506 lb/inÂ³
Linear Mold Shrinkage, Flow	0.020 - 0.023 cm/cm	0.020 - 0.023 in/in
Linear Mold Shrinkage, Transverse	0.0205 - 0.0225 cm/cm	0.0205 - 0.0225 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	55.0 MPa	7980 psi
Elongation at Break	5.0 %	5.0 %
Tensile Modulus	3.00 GPa	435 ksi
Charpy Impact Unnotched	3.50 J/cmÂ²	16.7 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	135 Â°C	275 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	85.0 Â°C	185 Â°F
Vicat Softening Point	150 Â°C @Load 5.00 kg	302 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1e+05	1e+05

Processing Properties	Metric	English
Melt Temperature	175 - 200 Â°C	347 - 392 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa