LATI Latiohm 75/4-10 CNT PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 75/4-10 CNT PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polybutylene Terephthalate (PBT). Carbon nanotubes. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.325 g/cc	0.04787 lb/inÂ³
Linear Mold Shrinkage, Flow	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in
Linear Mold Shrinkage, Transverse	0.017 - 0.020 cm/cm	0.017 - 0.020 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	60.0 MPa	8700 psi
Elongation at Break	10 %	10 %
Tensile Modulus	2.90 GPa	421 ksi
Charpy Impact Unnotched	9.00 J/cmÂ²	42.8 ft-lb/inÂ²
Charpy Impact, Notched	0.250 J/cmÂ²	1.19 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	170 Â°C	338 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	70.0 Â°C	158 Â°F
Vicat Softening Point	180 Â°C @Load 5.00 kg	356 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+8 ohm-cm	1.00e+8 ohm-cm
Surface Resistance	1.00e+8 ohm	1.00e+8 ohm

Processing Properties	Metric	English
Melt Temperature	240 - 260 Â°C	464 - 500 Â°F
Mold Temperature	60.0 - 85.0 Â°C	140 - 185 Â°F
Drying Temperature	120 - 130 Â°C @Time 10800 sec	248 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa