- HOME
- POLYMER SEARCH
- Thermoplastic
- Polystyrene (PS)
- SABIC Innovative Plastics NORYL PX1543 PPE+PS (Asia Pacific)
SABIC Innovative Plastics NORYL PX1543 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX1543 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.066 % @Time 86400 sec |
0.066 % @Time 24.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| 1.86 J/cm @Temperature -40.0 °C |
3.48 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C8080REC PC+ABS (Europe-Africa-Middle East)
- Polymer Resources ABS-GP-IM General Purpose ABS, Impact Modified
- SABIC HP0722N Low Density Polyethylene for Blown Film
- SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific)
- Westlake Elevate™ EF437 2.5% Ethylene Vinyl Acetate Copolymer
- DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612 (Unverified Data**)
- Chosun Refractories HSC-16H-W2 Dense and High-Strength Castable, Credens
- Braskem TI2900C High Crystallinity Copolymer Polypropylene
- Asahi Kasei Leona® 1300F Nylon 66
- 3M 8427-6 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved