LATI Latilub 73/13-15T G/15 POM, 15% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer + Glass/PTFE
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 73/13-15T G/15 POM, 15% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyoxymethylene (POM). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Linear Mold Shrinkage, Transverse 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
Elongation at Break 1.8 %
1.8 %
Tensile Modulus 5.60 GPa
812 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Coefficient of Friction, Dynamic 0.19
0.19
Coefficient of Friction, Static 0.25
0.25
K (wear) Factor 45.0 x 10-8 mm³/N-M
22.3 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point 150 °C

@Load 5.00 kg
302 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 175 - 200 °C
347 - 392 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa