LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene copolymer (PPc) based compound. UV stabilized. Improved thermal stabilization. Special mineral filler. Very good surface appearance. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.011 - 0.014 cm/cm | 0.011 - 0.014 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0115 - 0.0145 cm/cm | 0.0115 - 0.0145 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | >= 100 % @Temperature 23.0 °C |
>= 100 % @Temperature 73.4 °F |
|
| >= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
| Elongation at Yield | 8.0 % @Temperature 23.0 °C |
8.0 % @Temperature 73.4 °F |
|
| 10 % @Temperature 60.0 °C |
10 % @Temperature 140 °F |
||
| Tensile Modulus | 0.500 GPa @Temperature 90.0 °C |
72.5 ksi @Temperature 194 °F |
|
| 1.00 GPa @Temperature 60.0 °C |
145 ksi @Temperature 140 °F |
||
| 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 80.0 °C @Load 5.00 kg |
176 °F @Load 11.0 lb |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- RheTech Products HP532-00 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Natural
- Mueller Dynalloy Alloy 6730 Free cutting bearing bronze (UNS C67300)
- Silberline Sparkle Silvex® Premier 890-20-D
- SABIC Innovative Plastics LNP VERTON RVL29 PA 66
- Polyplastics FR-PET® C9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
- Arkema Group Orevac® 9304 Film EVA-MAH Terpolymer
- 3M 3195-EZ Polyethylene Protective Tapes
- Austin Novel Materials Texalan® 682A Polyester and Polyether based TPU
Copyright © lookpolymers.com All Rights Reserved