LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0025 - 0.0050 cm/cm | 0.0025 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa @Temperature 90.0 °C |
5800 psi @Temperature 194 °F |
|
| 65.0 MPa @Temperature 60.0 °C |
9430 psi @Temperature 140 °F |
||
| 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
||
| Elongation at Break | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
|
| 3.4 % @Temperature 60.0 °C |
3.4 % @Temperature 140 °F |
||
| 5.8 % @Temperature 90.0 °C |
5.8 % @Temperature 194 °F |
||
| Elongation at Yield | 2.7 % @Temperature 60.0 °C |
2.7 % @Temperature 140 °F |
|
| 4.2 % @Temperature 90.0 °C |
4.2 % @Temperature 194 °F |
||
| Tensile Modulus | 5.30 GPa @Temperature 90.0 °C |
769 ksi @Temperature 194 °F |
|
| 8.20 GPa @Temperature 60.0 °C |
1190 ksi @Temperature 140 °F |
||
| 10.0 GPa @Temperature 23.0 °C |
1450 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.80 J/cm² @Temperature -20.0 °C |
8.57 ft-lb/in² @Temperature -4.00 °F |
|
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
|
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 140 °C @Load 5.00 kg |
284 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 715-10 Reactive Alumina
- Lanxess Pocan® B 7425 000000 PBT, 20% Glass Spheres
- Lehmann & Voss LUVOCOM® 1104-7598 Polyether ketone, with carbon fiber, PTFE, lubricant modified
- Multibase Multibatch® MP 50004 Anti-split
- ExxonMobil PP3155E3 Polypropylene Copolymer
- Aaron Industries AAROLENE® ARPE LD 300-1 Low Density Polyethylene Compounded Resin
- Cast Nylons Nycast® Nyloil®-MDX Lubricated Nylon, MoS2 Filled
- Crucible Steel REX® M7N High Speed Steel, AISI M7
Copyright © lookpolymers.com All Rights Reserved