Techmer ES Elastoblend® PA12 CL
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA12 CL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAppearance: Clear/TransparentInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 230 °C |
12 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 81.4 MPa | 11800 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 98.6 MPa | 14300 psi | ASTM D790 |
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Poissons Ratio | 0.40 | 0.40 | ASTM E132 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate B (120°C/h); ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.70 % | 0.70 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| IR Transmittance | 89 - 90 % | 89 - 90 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® 7-6860 Dow-Corning Biomedical Grade Liquid Silicone Rubber
- Osprey Metals 317L Stainless Steel Powder (Grade 90% - 16)
- Solvay Chemicals CASO® TEC SOLUTION 25-29% Calcium Chloride
- Techmer ES Luriblend® PC CF10 TL10 BK 10% Carbon Filled
- Silberline Silcroma® BG-15
- Braskem Green PE SHE150 Blown Film Extrusion and Cast Film Extrusion High Density Polyethylene
- Barlog Plastics KEBAFORM C 901 SO POM Copolymer unreinforced, improved wear and friction
- Axion Polymers Axpoly® PS01 3000 General Purpose Polystyrene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N990 (MT) Filler
Copyright © lookpolymers.com All Rights Reserved