Samsung Cheil Industries Infino® CF-3104HF PC, 10% Glass Filled High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled , Polycarbonate, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® CF-3104HF PC, 10% Glass Filled High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-impact PC/GR material for the exterior of slim mobile phoneInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 23 g/10 min @Load 10.0 kg, Temperature 250 °C |
23 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 93.2 MPa | 13500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.94 GPa | 427 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.75 J/cm @Thickness 3.17 mm |
5.14 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C @Thickness 6.40 mm |
286 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 137 °C | 279 °F | B/50; ISO R306 |
| Flammability, UL94 | 2.00 @Thickness 3.20 mm |
2.00 @Thickness 0.126 in |
|
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6/66 FRc 3 TS PA6/66, flame retardant
- Kinlead ML11 General Grade BOPP Matt Film (thickness: 18 µm)
- Momentive Performance Materials Siloprenâ„¢ Electro 242-2 Electrically Insulating Liquid Silicone Rubber
- Momentive Performance Materials Siloprenâ„¢ LSR 4640 Liquid Silicone Rubber - Healthcare
- Tipco Tipcolene® X 408 IN - 10% Talc/Mineral Reinforced Polypropylene Copolymer, Very High Impact Strength & Flow
- EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass
- Addiplast Addilene H 526 N30 Polypropylene Homopolymer
- BASF Heligoen® Blue 6989 F Color Additive
- A. Schulman ComAlloy Hiloy® 221 ABS, Glass Reinforced, UL
- LATI Laticonther 62 CEG/500-V0HF1 PA 6, Glass/Mineral Reinforced, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved