- Lanxess Pocan® T 3150 XF 000000 PBT + PET, 55% Glass Fiber
Lanxess Pocan® T 3150 XF 000000 PBT + PET, 55% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® T 3150 XF 000000 PBT + PET, 55% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PET, 55% glass fibers, injection molding, improved flowability, low tendency to warp, increased temperature peak load, increased strength and increased modulus
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Melt Flow | 34 g/10 min @Load 5.00 kg, Temperature 270 °C |
34 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1/-2 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1/-2 |
| Tensile Modulus | 18.5 GPa | 2680 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 - 260 °C | 437 - 500 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 |
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT+PET,GHMR,07-190,GF55 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nylene® 9110 G33 , 33% Glass Reinforced Nylon 6/10
- BASF Capron® B100MP Nylon 6 (DAM) (discontinued **)
- Greene Tweed CHEMRAZ® 510 Perfluoroelastomer
- SPHERE ONE EXTENDOSPHERESâ„¢ 300/600 Hollow Spheres
- DSM Stanyl® TE250F3 Nylon 46-15% Glass Reinforced (European and Asian Grade) (Cond)
- Denka MALECCA K-090 ABS
- Aaron Industries AAROPRENE® GFPC 5010 Glass Filled Polycarbonate
- Carpenter Chrome Core® 12-FM Alloy
- ExxonMobil Mobilarma 798
Copyright © lookpolymers.com All Rights Reserved