ExxonMobil Bicor™ 70 XRG-2 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 70 XRG-2 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 70 XRG-2 is one-side treated, one-side sealable OPP film that can be used as the inside web of a lamination where exceptional seal performance is required. The high-energy surface is intended as the print and laminating side.Availability: Latin America, North America and South AmericaKey Features:Low MST, very broad seal range with excellent hot tackHigh-energy surface for excellent ink adhesion and bond strengths in adhesive and extrusion laminationsLap seals to coex sealants without thermal stripeFeatures:In Lamination Lap SealableVery Broad Seal RangeApplications:BakeryBiscuits/Cookie/Crackers Crisps and SnacksFrozen FoodIce CreamUses:HFFS Flexible Packaging VFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 17.8 microns | 0.700 mil | ExxonMobil Method |
| Coating Weight | 15.7 g/m² | 9.80 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 165 % | 165 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 47 % | 47 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Coefficient of Friction | 0.40 | 0.40 | Untreated; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 283 MPa | 41000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % @Temperature 135 °C |
4.5 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 4.0 % @Temperature 135 °C |
4.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.6 % | 2.6 % | ExxonMobil Method |
| Gloss | 84 % | 84 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 89°C | Untreated |
| Crimp Seal Strength | 400 g/in | Treated/Treated, 240°F (116°C), 20 psi (0.1 MPa), 0.8 sec |
| 400 g/in | Untreated/Untreated, 240°F (116°C), 20 psi (0.1 MPa), 0.8 sec | |
| Wetting Tension | 0.8 receding cos theta | Treated Surface |
| Yield | 41000 in2/lb |
Users viewing this material also viewed the following:
- Noble Polymers Regis™ 125098 Thermoplastic Olefin (TPO)
- Fine Organics FINALUX G 785 Lubricant Additive
- Special Metals INCONEL® alloy 783 Ni-Co-Fe Alloy
- Techmer ES HiFill® PA6 L N MB (Dry)
- Unifrax Fiberfrax® Duraback® Ceramic Fiber Insulator
- DuPont™ Elvax® 3155 Ethylene Vinyl Acetate
- Arkema Group Orgalloy® LE 6000 Nylon Alloy, Flexible Grade (Conditioned)
- Ascend Performance Materials Vydyne® 47 Nylon 66, Conditioned
- Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved