LATI Latene® AG7H G/30 PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latene® AG7H G/30 PP Homopolymer, 30% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Glass fibers. Good thermal propertiesAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa @Temperature 90.0 °C |
5800 psi @Temperature 194 °F |
|
| 55.0 MPa @Temperature 60.0 °C |
7980 psi @Temperature 140 °F |
||
| 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 3.5 % @Temperature 60.0 °C |
3.5 % @Temperature 140 °F |
||
| 6.0 % @Temperature 90.0 °C |
6.0 % @Temperature 194 °F |
||
| Tensile Modulus | 3.30 GPa @Temperature 90.0 °C |
479 ksi @Temperature 194 °F |
|
| 4.50 GPa @Temperature 60.0 °C |
653 ksi @Temperature 140 °F |
||
| 6.30 GPa @Temperature 23.0 °C |
914 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Vicat Softening Point | 135 °C @Load 5.00 kg |
275 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Time 10800 sec |
176 - 194 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- PolyOne Dynalloy™ OBC 8100-N65 Thermoplastic Elastomer (TPE)
- Ineos ABS Lustran® ABS 241 ABS, Blending Grade
- Lord Adhesives Thermosetâ„¢ MD-110 Conductive Adhesive
- TIMCAL TIMREX® FC250 Coke
- Hippe PF CC 203 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet
- Fainplast Compounds GS 7216 Flexible PVC, Injection Molding for Footwear
- Adamas Adalon® 209 PTFE, 15% Glass Filled
- Ashley Polymers Ashlene® 527LD-45LG Nylon 66, 45% Long Glass Fiber Reinforced
- Solvay RHODAPHOSE® VDPA (WET CAKE) Phosphorus derivative
Copyright © lookpolymers.com All Rights Reserved