- Polykemi AB POLYshine PBT C213 GF15 FR PBT, Glass Fiber-Reinforced, Flame Retardant
Polykemi AB POLYshine PBT C213 GF15 FR PBT, Glass Fiber-Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | POLYshine |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYshine PBT C213 GF15 FR PBT, Glass Fiber-Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ±2%; Polykemi |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 90.0 MPa | <= 13100 psi | ISO/R527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 136 MPa | <= 19700 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa @Temperature 23.0 °C |
754 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 189 °C @Load 5.001 kg |
372 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 215 °C @Load 1.00 kg |
419 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A12^ Nylon 66
- Plastcom SLOVALEN PH 49 GF 30 003/3M Polypropylene reinforced with glass fiber, heat stabilized
- DSM Biomedical PurSil® AL 5 Aliphatic Thermoplastic Silicone Polyether Urethane (discontinued **)
- Kraton® D1102 K (SBS) Liner Block Copolymer
- Momentive Performance Materials Siloprenâ„¢ LIM 6071 Liquid Silicone Rubber - Fast Cure / High Tear
- Haynes Multimet® alloy, GTAW, 9.5 mm plate
- Haynes Ultimet® alloy, mill annealed
- China Tungsten YT770 Tungsten Carbide
- DuPont Teijin Films Mylar® E Polyester Film, 142 Gauge
- AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition C
Copyright © lookpolymers.com All Rights Reserved