LATI Latan 3E71 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	LATI
Trade Name	Latan
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latan 3E71 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyoxymethylene (POM). Toughened. High viscosity. Good elongation and impact resistanceAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.36 g/cc	0.0491 lb/inÂ³
Linear Mold Shrinkage, Flow	0.023 - 0.027 cm/cm	0.023 - 0.027 in/in
Linear Mold Shrinkage, Transverse	0.0235 - 0.0275 cm/cm	0.0235 - 0.0275 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	>= 100 % @Temperature 23.0 Â°C	>= 100 % @Temperature 73.4 Â°F
	>= 100 % @Temperature 60.0 Â°C	>= 100 % @Temperature 140 Â°F
	>= 100 % @Temperature 90.0 Â°C	>= 100 % @Temperature 194 Â°F
Tensile Modulus	0.650 GPa @Temperature 90.0 Â°C	94.3 ksi @Temperature 194 Â°F
	1.10 GPa @Temperature 60.0 Â°C	160 ksi @Temperature 140 Â°F
	1.90 GPa @Temperature 23.0 Â°C	276 ksi @Temperature 73.4 Â°F
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	1.20 J/cmÂ²	5.71 ft-lb/inÂ²

Thermal Properties	Metric	English
Maximum Service Temperature, Air	70.0 Â°C	158 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	145 Â°C	293 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	75.0 Â°C	167 Â°F
Vicat Softening Point	125 Â°C @Load 5.00 kg	257 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	A solution

Processing Properties	Metric	English
Melt Temperature	175 - 200 Â°C	347 - 392 Â°F
Mold Temperature	60.0 - 90.0 Â°C	140 - 194 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa