LATI Latan 13 S/30 POM, 30% Glass Bead Reinforced

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled
Manufacturer LATI
Trade Name Latan
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latan 13 S/30 POM, 30% Glass Bead Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
Linear Mold Shrinkage, Flow 0.017 - 0.020 cm/cm
0.017 - 0.020 in/in
Linear Mold Shrinkage, Transverse 0.017 - 0.0195 cm/cm
0.017 - 0.0195 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 60.0 °C
 3630 psi

@Temperature 140 °F
35.0 MPa

@Temperature 23.0 °C
 5080 psi

@Temperature 73.4 °F
Elongation at Break 20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
65 %

@Temperature 60.0 °C
 65 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
Elongation at Yield 5.5 %

@Temperature 23.0 °C
 5.5 %

@Temperature 73.4 °F
6.0 %

@Temperature 60.0 °C
 6.0 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
Tensile Modulus 1.30 GPa

@Temperature 90.0 °C
 189 ksi

@Temperature 194 °F
2.30 GPa

@Temperature 60.0 °C
 334 ksi

@Temperature 140 °F
3.60 GPa

@Temperature 23.0 °C
 522 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
3.80 J/cm²

@Temperature -20.0 °C
 18.1 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.150 J/cm²

@Temperature 23.0 °C
 0.714 ft-lb/in²

@Temperature 73.4 °F
0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
Vicat Softening Point 150 °C

@Load 5.00 kg
 302 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa