LATI Latamid 6 H2 G/20-V2HF PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/20-V2HF PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.0065 - 0.0090 cm/cm
0.0065 - 0.0090 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0080 cm/cm
0.0055 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa

@Temperature 150 °C
 2180 psi

@Temperature 302 °F
30.0 MPa

@Temperature 120 °C
 4350 psi

@Temperature 248 °F
35.0 MPa

@Temperature 90.0 °C
 5080 psi

@Temperature 194 °F
60.0 MPa

@Temperature 60.0 °C
 8700 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
Elongation at Break 3.5 %

@Temperature 23.0 °C
 3.5 %

@Temperature 73.4 °F
4.3 %

@Temperature 60.0 °C
 4.3 %

@Temperature 140 °F
7.0 %

@Temperature 90.0 °C
 7.0 %

@Temperature 194 °F
9.0 %

@Temperature 120 °C
 9.0 %

@Temperature 248 °F
15 %

@Temperature 150 °C
 15 %

@Temperature 302 °F
Elongation at Yield 3.2 %

@Temperature 90.0 °C
 3.2 %

@Temperature 194 °F
3.8 %

@Temperature 120 °C
 3.8 %

@Temperature 248 °F
4.5 %

@Temperature 150 °C
 4.5 %

@Temperature 302 °F
Tensile Modulus 1.70 GPa

@Temperature 150 °C
 247 ksi

@Temperature 302 °F
2.10 GPa

@Temperature 120 °C
 305 ksi

@Temperature 248 °F
2.60 GPa

@Temperature 90.0 °C
 377 ksi

@Temperature 194 °F
4.20 GPa

@Temperature 60.0 °C
 609 ksi

@Temperature 140 °F
5.50 GPa

@Temperature 23.0 °C
 798 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 27 %
27 %
Glow Wire Test 725 °C

@Thickness 1.00 mm
 1340 °F

@Thickness 0.0394 in
 GWIT
725 °C

@Thickness 2.00 mm
 1340 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa