LATI Lastilac AR G/17-V0E ABS, 17% Glass Fiber Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
Manufacturer LATI
Trade Name Lastilac
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lastilac AR G/17-V0E ABS, 17% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Acrylonitrile-Butadiene-Styrene copolymer (ABS) based compound. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 8.00 MPa

@Temperature 90.0 °C
 1160 psi

@Temperature 194 °F
15.0 MPa

@Temperature 60.0 °C
 2180 psi

@Temperature 140 °F
35.0 MPa

@Temperature 23.0 °C
 5080 psi

@Temperature 73.4 °F
Elongation at Break 1.5 %

@Temperature 23.0 °C
 1.5 %

@Temperature 73.4 °F
1.5 %

@Temperature 60.0 °C
 1.5 %

@Temperature 140 °F
15 %

@Temperature 90.0 °C
 15 %

@Temperature 194 °F
Elongation at Yield 1.0 %

@Temperature 90.0 °C
 1.0 %

@Temperature 194 °F
Tensile Modulus 2.90 GPa

@Temperature 90.0 °C
 421 ksi

@Temperature 194 °F
3.90 GPa

@Temperature 60.0 °C
 566 ksi

@Temperature 140 °F
4.70 GPa

@Temperature 23.0 °C
 682 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
1.00 J/cm²

@Temperature -20.0 °C
 4.76 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 70.0 °C
158 °F
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Vicat Softening Point 85.0 °C

@Load 5.00 kg
 185 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 0.750 mm
 V-1

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 36 %
36 %
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 GWIT
800 °C

@Thickness 2.00 mm
 1470 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 325 V
325 V
A solution
Processing Properties Metric English Comments
Melt Temperature 190 - 220 °C
374 - 428 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 70.0 - 80.0 °C

@Time 10800 sec
 158 - 176 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa