SABIC Innovative Plastics LNP THERMOCOMP MF002S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF002S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 | |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| 5.8 % | 5.8 % | 5 mm/min; ISO 527 | |
| 6.7 % | 6.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.97 GPa | 431 ksi | 1 mm/min; ISO 527 |
| 2.98 GPa | 432 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| 75.0 MPa | 10900 psi | ASTM D790 | |
| Flexural Modulus | 2.33 GPa | 338 ksi | 2 mm/min; ISO 178 |
| 2.39 GPa | 347 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 2.87 GPa | 416 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.88 J/cm | 9.14 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 88.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 154 °C @Thickness 3.20 mm |
309 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Radici Radilon® A RV330 (cond.) Nylon 66
- Huntsman IROGRAN® A 95 P 5044 DP TPU-Polyether
- H.C. Starck Amperit® 109.063 Agglomerated Sintered Molybdenum (Mo)
- Sylvin Technologies 9077-90 LMW Natural PVC for Injection Molding
- Stellarchem MP-930HD TPE Compound
- Shin-Etsu Silicones KF-8018 Fluid
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- ExxonMobil Metallyte® 70 MET OPP Film
- DuPont Teijin Films Melinex® 535 Polyester Film
- PolyOne Edgetek® PF-10GF/000 Polysulfone, Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved