LATI LATAMID 12 H FE85 Nylon 12 Base Magnetizable Compound  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LATAMID 12 H FE85 Nylon 12 Base Magnetizable Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: These are compounds containing a high percentage of magnetizable fillers; compared to traditional techniques for the manufacture of magnets, this allows the molding of complex shapes using injection molding. To obtain permanent magnetization values, molded parts must then be submitted to the action of a magnetic field. All magnetizable LATI thermoplastics are 'hard' magnetic materials of the permanent type which will therefore require high demagnetizing power (high Hc). Magnetic values shown in the charts are obtained on molded parts using traditional processing methods; for particular requirements, higher values may be obtained using special techniques. APPLICATIONS: deflection yokes for TV sets, parts for small electric motors, components for meters and video-recorders, permanent magnets for various applications. Specific Notes for this Material: PA 12 base; fair flowability; high contents of special magnetizable fillers for superior magnetic performances, especially with orientation during molding.Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 3.25 g/cc
0.117 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
LATI
Mechanical Properties Metric English Comments
Flexural Modulus 10.5 GPa
1520 ksi
ASTM D790
Izod Impact, Notched 0.310 J/cm

@Temperature 23.0 °C
0.581 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C
306 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ASTM D648
Vicat Softening Point 165 °C
329 °F
50°C/h 50N; ISO 306
Electrical Properties Metric English Comments
Comparative Tracking Index 295 V
295 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Keep the material always warm in a hopper at 70-80°C. Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Injection Speed medium