LG Chemical LUTENE FB0300 LDPE Blown Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE FB0300 LDPE Blown Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE FB0300 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of heavy duty sacks and pallet shrink films. LUTENE FB0300 have the excellent mechanical properties and high stress cracking resistance make suitable for heavy duty bags and particularity bottom sealed bags. (LUTENE FB0300 contains no slip agent.)Main Application: Packing of heavy products, Shrink hoods, Pallet shrink covers, all types of industrial packingCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 |
| Water Vapor Transmission | 10.0 g/m²/day | 0.644 g/100 in²/day | |
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50; ASTM D1693 |
| Thickness | 20.0 - 100 microns | 0.787 - 3.94 mil | |
| 50.0 - 300 microns | 1.97 - 11.8 mil | ||
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Tear Strength | 363 kN/m | 2070 pli | MD; ASTM D1922 |
| 373 kN/m | 2130 pli | TD; ASTM D1922 | |
| Dart Drop Test | 300 g | 0.662 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.5 MPa | 3410 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.6 MPa | 3280 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | DSC |
| Crystallization Temperature | 104 °C | 219 °F | ASTM D1525 |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D740 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 60°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 - 220 °C | 374 - 428 °F | |
| Blow-up Ratio (BUR) | 1.5 - 2.0 | 1.5 - 2.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Slip Coefficient | 0.47 | ASMT D1894 |
Users viewing this material also viewed the following:
- RheTech Products FT4900-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- LG Chemical LUPOY GP-5306F General Purpose PC/ABS Alloy, 30% Polymer Alloy, Weather Resistant, Flame Retardant
- Lucent Polymers GPCB-110 Polycarbonate+PBT, 10% Glass Fiber Reinforced
- Techmer ES HiFill® PA6/6 GF/M15 HS L BK 40/15% Glass/Mineral Fiber Filled
- Solvay JAGUAR® C 500 Surfactant
- DuPont Performance Polymers Crastin® 6129 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- ExxonMobil LLDPE LLP 8555.24 Linear Low Density Polyethylene Resin
- Diamond Polymers ABS 7502
Copyright © lookpolymers.com All Rights Reserved