Oxford Polymers PC 912 Unfilled Polycarbonate for Injection and Extrusion Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers PC 912 Unfilled Polycarbonate for Injection and Extrusion Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled Polycarbonate for Injection and Extrusion MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 124 % | 124 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Compressive Strength | 86.2 MPa | 12500 psi | ASTM D695 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 282 °C | 540 °F |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP200R Injection Molding Grade Polypropylene
- Overview of materials for Nylon 610, Glass Reinforced
- Sylvin Technologies 9077-75 Natural PVC for Injection Molding
- Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C)
- SABIC Innovative Plastics Xenoy® X6800BM PBT (Asia Pacific)
- Teknor Apex Fireguard® 910-A10-NL2 Polyvinyl Chloride, Flexible
- CLAL-MSX ARCAP Anticorrosion AP4 H13 3/4 hard, Drawn Copper Alloy
- A. Schulman ComAlloy Hiloy® 124 Polypropylene, Glass Reinforced, Chemically Coupled
- Lucky EH-910 Acrylic, Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved