Kolon DIAMAT® EH
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Extruded |
| Manufacturer | Kolon |
| Trade Name | DIAMAT® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon DIAMAT® EH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonable pricing. DIAMAT® utilizes acrylic toughener technology resulting in consistent appearance, even after years of UV exposure. DIAMAT® EH is a resin for extrusion molding with excellent impact strength. Information provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 45 | 45 | ASTM D785 |
| Tensile Strength, Ultimate | 39.2 MPa | 5690 psi | ASTM D638 |
| Flexural Strength | 63.4 MPa | 9200 psi | ASTM D790 |
| Flexural Modulus | 1.77 GPa | 256 ksi | ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 20.6 J | 15.2 ft-lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | Load not specified; ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Glass Transition Temp, Tg | 105 °C | 221 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 - 180 °C | 302 - 356 °F | Injection |
| Middle Barrel Temperature | 180 - 230 °C | 356 - 446 °F | Injection |
| Front Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection |
| Nozzle Temperature | 220 - 245 °C | 428 - 473 °F | Injection |
| Zone 1 | 200 - 220 °C | 392 - 428 °F | Extrusion |
| Zone 2 | 210 - 230 °C | 410 - 446 °F | Extrusion |
| Zone 3 | 220 - 240 °C | 428 - 464 °F | Extrusion |
| Zone 4 | 210 - 235 °C | 410 - 455 °F | Vent; Extrusion |
| Zone 5 | 225 - 240 °C | 437 - 464 °F | Extrusion |
| Adapter Temperature | 230 - 240 °C | 446 - 464 °F | Extrusion |
| Die Temperature | 220 - 240 °C | 428 - 464 °F | Extrusion |
| Melt Temperature | 220 - 235 °C | 428 - 455 °F | Recommended for Injection |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Roll Temperature | 80.0 - 100 °C | 176 - 212 °F | Extrusion |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Injection Pressure | 78.45 - 137.3 MPa | 11380 - 19910 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | Extrusion |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® GPM5500U ABS (Europe-Africa-Middle East)
- Pyrotek V-5 Fiberglass Fabric
- Hardwire 3SX-12-12 Medium Density Tape
- TIMCAL TIMREX® T200-2000 Primary Synthetic Graphite
- Alliance N-40M Neodymium Iron Boron Magnetic Material
- 3M FP024802 Clear Polypropylene Label Products
- 3M K1 Glass Bubbles
- Arlon 32580R060 0.060" (1.52 mm) Uncured Silicone Rubber on PET Carrier
- Goodfellow Aluminum 75/Silicon 25 Alloy
Copyright © lookpolymers.com All Rights Reserved