- Eurotec® Tecolen® CP10 GR15 NL PPCP, 15% glass fiber reinforced, natural
Eurotec® Tecolen® CP10 GR15 NL PPCP, 15% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Eurotec |
| Trade Name | Tecolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecolen® CP10 GR15 NL PPCP, 15% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 3.25 GPa | 471 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 165 °C | 320 - 329 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 240 °C | 392 - 464 °F | |
| Feed Temperature | <= 60.0 °C | <= 140 °F | Throat |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3672 TPE, PP Overmold or Standalone use
- Freudenberg Simrit V178 Non-Black Compound
- SABIC Innovative Plastics ULTEM 1110F PEI (Asia Pacific)
- SGL Carbon Group Ridurid® EK 60 High Performance Graphite Filled Plastic
- Stratasys® Ultem 9085 for Rapid Prototyping
- SABIC Innovative Plastics LNP THERMOCOMP RF008XXZ PA 66
- E-Polymers TEKAMID® TB110M40 , 40% Mineral Filled PA6, DAM
- 3M 7218SA Screen Printable Polyester Performance Label Products with Structured Adhesive
- Fainplast Compounds PH 90/A Flexible PVC, Transparent Extrusion
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction
Copyright © lookpolymers.com All Rights Reserved