Kingfa HF-606 Flame Retardant ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer	Kingfa Sci. & Tech. Co.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kingfa HF-606 Flame Retardant ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features:UL 94 V-0 @ 1.6-3.0mm, 5VB @ 2.0mmHigh flowModerate UV stabilityHigh stiffnessApplications:Injection moldingMonitor cabinetCD-ROMPower switchInformation Provided by Kingfa Sci. & Tech. Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc @Temperature 23.0 Â°C	1.18 g/cc @Temperature 73.4 Â°F	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm @Temperature 23.0 Â°C	0.0040 - 0.0060 in/in @Temperature 73.4 Â°F	ASTM D955
Melt Flow	6.0 g/10 min @Load 5.00 kg, Temperature 200 Â°C	6.0 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
	65 g/10 min @Load 10.0 kg, Temperature 220 Â°C	65 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	104	104	ASTM D785
Tensile Strength at Break	43.0 MPa	6240 psi	50mm/min; ASTM D638
Elongation at Break	10 %	10 %	50mm/min; ASTM D638
Flexural Strength	66.0 MPa	9570 psi	2mm/min; ASTM D790
Flexural Modulus	2.40 GPa	348 ksi	2mm/min; ASTM D790
Izod Impact, Notched	1.63 J/cm @Thickness 6.40 mm, Temperature 23.0 Â°C	3.05 ft-lb/in @Thickness 0.252 in, Temperature 73.4 Â°F	ASTM D256
	1.96 J/cm @Thickness 3.20 mm, Temperature 23.0 Â°C	3.67 ft-lb/in @Thickness 0.126 in, Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	85.0 Â°C @Thickness 6.40 mm	185 Â°F @Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	76.0 Â°C @Thickness 6.40 mm	169 Â°F @Thickness 0.252 in	ASTM D648
Vicat Softening Point	84.0 Â°C @Load 5.00 kg	183 Â°F @Load 11.0 lb	50Â°C/min; ASTM D1525
	93.0 Â°C @Load 1.00 kg	199 Â°F @Load 2.20 lb	120Â°C/min; ASTM D1525
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in
	5VB @Thickness 2.00 mm	5VB @Thickness 0.0787 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D257
Dielectric Strength	22.0 kV/mm	559 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Processing Temperature	<= 230 Â°C	<= 446 Â°F
Rear Barrel Temperature	160 - 180 Â°C	320 - 356 Â°F	Start Point: 170Â°C
Middle Barrel Temperature	170 - 190 Â°C	338 - 374 Â°F	Start Point: 180Â°C
Front Barrel Temperature	180 - 210 Â°C	356 - 410 Â°F	Start Point: 190Â°C
Melt Temperature	170 - 210 Â°C	338 - 410 Â°F	Start Point: 190Â°C
Mold Temperature	30.0 - 60.0 Â°C	86.0 - 140 Â°F	Start Point: 50Â°C
Drying Temperature	70.0 - 80.0 Â°C @Time 7200 - 14400 sec	158 - 176 Â°F @Time 2.00 - 4.00 hour	Pre-dry
Back Pressure	0.000 - 1.00 MPa	0.000 - 145 psi

Descriptive Properties	Value	Comments
Injection Speed	Slow to Moderate