Ineos ABS Lustran® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lustran® Ultra 4000 PG is electroplating grade with high heat resistance. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Test Condition: 150x105x3; acc. ISO 2577
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
ISO 2039-1
Tensile Strength, Yield 46.0 MPa
6670 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 15 %
>= 15 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 3.1 %
3.1 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 73.0 MPa
10600 psi
2 mm/min; ISO 178
Flexural Modulus 2.35 GPa
341 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
23.0 kJ/m²

@Temperature 23.0 °C
 10.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 103 °C
217 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ISO 75-1,-2
Vicat Softening Point 107 °C

@Load 5.10 kg
 225 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 38.0 kV/mm

@Thickness 1.00 mm
 965 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.0063

@Frequency 100 Hz
 0.0063

@Frequency 100 Hz
 IEC 60250
0.0087

@Frequency 1.00e+6 Hz
 0.0087

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294