SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* V1000UXC is a compound based on Nylon resin. Added features of this material include: UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Density | 1.065 g/cc | 0.03848 lb/in³ | ASTM D792 |
| 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.021 - 0.023 cm/cm @Time 86400 sec |
0.021 - 0.023 in/in @Time 24.0 hour |
ASTM D955 |
| 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.025 - 0.027 cm/cm @Time 86400 sec |
0.025 - 0.027 in/in @Time 24.0 hour |
ASTM D955 |
| 0.026 cm/cm @Time 86400 sec |
0.026 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 84.5 % | 84.5 % | Type I, 5 mm/min; ASTM D638 |
| 165 % | 165 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 57.2 % | 57.2 % | Type I, 5 mm/min; ASTM D638 |
| 146.7 % | 146.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 1.65 GPa | 239 ksi | 1 mm/min; ISO 527 |
| 1.71 GPa | 248 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 53.0 MPa | 7690 psi | ISO 178 |
| 55.0 MPa | 7980 psi | ASTM D790 | |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| 2.06 GPa | 299 ksi | ASTM D790 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 49.0 J @Temperature 23.0 °C |
36.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 49.0 J | 36.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 134 µm/m-°C @Temperature -40.0 - 40.0 °C |
74.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 135 µm/m-°C @Temperature -40.0 - 40.0 °C |
75.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature -40.0 - 40.0 °C |
73.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 134 µm/m-°C @Temperature -40.0 - 40.0 °C |
74.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 192 °C @Thickness 3.20 mm |
378 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 940A PC (Europe-Africa-Middle East)
- Kazanorgsintez Cosintol 242
- Lehmann & Voss LUVOCOM® 50-7164/BL02 Polycarbonate, with glass fiber and PTFE
- A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene
- Hexcel® HexWeb® HRH-10 - 3/16 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb
- Crucible Steel CSM® S60V (440V) Tool Steel, AISI 440C Modified
- Eurostar Staramide AG3 PA66, 15% Glass Filled, Injection Molded
- ATI Allvac® Vasco® 17-4 Precipitation Hardening Steel, Heat Treatment: 1038°C (1900°F) + Age
- Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion
- Amity Thermosets ATS 157 Phenolic Molding Long glass fiber Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved