- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Ineos ABS Lustran® ABS 970
Ineos ABS Lustran® ABS 970
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 970.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 970 has high impact strength and good paintability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 22 g/10 min @Load 10.0 kg, Temperature 220 °C |
22 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ISO 2039-2 |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 2.25 GPa | 326 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 17.0 kJ/m² @Temperature -20.0 °C |
8.09 ft-lb/in² @Temperature -4.00 °F |
ISO 180-1A | |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1,-2 |
| Vicat Softening Point | 98.0 °C @Load 5.10 kg |
208 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 89 % | 89 % | Angle 60°; ISO 2813 |
Users viewing this material also viewed the following:
- Nye Lubricants 132H (SO) Synthetic Oil
- Chevron Phillips MarFlex® ER3341 Polyethylene; Masterbatch (discontinued **)
- Honeywell Aegis™ HCA73MP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- LG Chemical Lupox® PBT-GP-2156F 15% GFR Flame Retardant PBT
- Shin-Etsu Silicones KE-3421 Silicone, RTV Conformal Coating
- Teknor Apex APEX® 3301-70 Polyvinyl Chloride, Flexible
- Loctite® Durabond® E-40FL Epoxy Adhesive
- Ensinger Tecapeek® XP-105 Compression Molded PEEK Compound, 15% Graphite Filled
- Aptek 7504LM-PMF UV Urethane Coating/Encapsulant
- Arlon 51756R028 Silicone Rubber/Fiberglass Laminate
Copyright © lookpolymers.com All Rights Reserved