Styrolution Luran® S 776 SE ASA

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer Styrolution
Trade Name Luran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® S 776 SE ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Luran S 776 SE is a general purpose extrusion ASA grade with good toughness and strength, used for sheet and profile extrusions.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Water Absorption 1.65 %
1.65 %
ISO 62
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
ASTM Data; MD
Melt Flow 4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
4.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 4.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM Test
Mechanical Properties Metric English Comments
Hardness, Rockwell R 89
89
ASTM Test
Tensile Strength, Yield 33.0 MPa
4790 psi
2 in/min; ASTM Test
18.0 MPa

@Temperature 80.0 °C
 2610 psi

@Temperature 176 °F
 ISO Data
Elongation at Break 49 %
49 %
2 in/min; ASTM Test
Elongation at Yield 2.7 %
2.7 %
2 in/min; ASTM Test
1.9 %

@Temperature 80.0 °C
 1.9 %

@Temperature 176 °F
 ISO Data
Tensile Modulus 1.65 GPa
239 ksi
ASTM Test
Flexural Strength 47.0 MPa
6820 psi
ASTM Test
Flexural Modulus 1.66 GPa
241 ksi
ASTM Test
Izod Impact, Notched 0.510 J/cm

@Temperature -40.0 °C
 0.955 ft-lb/in

@Temperature -40.0 °F
 ASTM Test
2.60 J/cm

@Thickness 3.17 mm
 4.87 ft-lb/in

@Thickness 0.125 in
 ASTM Test
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C
52.8 µin/in-°F
ISO 11359
110 µm/m-°C
61.1 µin/in-°F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 101 °C
214 °F
annealed; ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
181 °F
annealed; ASTM Test
Vicat Softening Point 92.0 °C
198 °F
Rate "A" Loading 2 (50 degC/h 50N); ASTM Test
Flammability, UL94 HB

@Thickness 1.47 mm
 HB

@Thickness 0.0579 in
HB

@Thickness 0.810 mm
 HB

@Thickness 0.0319 in
Oxygen Index 19 %
19 %
ISO 4589-1/-2
Optical Properties Metric English Comments
Gloss 48 %
48 %
60° Specular; ASTM Test
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+13 ohm
>= 1.00e+13 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 IEC 60250
3.8

@Frequency 100 Hz
 3.8

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
 0.0090

@Frequency 100 Hz
 IEC 60250
0.034

@Frequency 1.00e+6 Hz
 0.034

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 230 - 270 °C
446 - 518 °F
Injection Molding
280 °C
536 °F
Injection molding
Mold Temperature 60.0 °C
140 °F
Injection molding
40.0 - 80.0 °C
104 - 176 °F
Injection Molding
Injection Velocity 200 mm/sec
7.87 in/sec
Injection molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2 - 4 hour
2 - 4 hour
Injection Molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Form Pellets
Impact Modified Yes
Injection Molding Regrind <30%
NSF Std. 51 No
NSF Std. 61 No
Primary Processing Technique Extrusion
Processing Blow Molding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Thermoforming
Special characteristic Heat stabilized or stable to heat
Light stabilized or stable to light
U.V. stabilized or stable to weather
UL.UL-C Yes
USP Class VI No