BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4406 G4 BKQ113 7110 is an UL V0 injection molding, pigmented black, PBT grade with 20% glass fiber reinforcement.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | 5mm/min; ISO 527 |
| 2.6 % | 2.6 % | ||
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1mm/min; ISO 527 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| 223 °C | 433 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK7110 | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Flame retarding agent | |
| Heat stabilized or stable to heat | ||
| Light stabilized or stable to light | ||
| Lubricant | ||
| U.V. stabilized or stable to weather |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2040MGHL Nylon 6 (Cond)
- SABIC Innovative Plastics LNP LUBRICOMP 5CL24 PVDF
- Teknor Apex Monprene® MP-2585B Thermoplastic Elastomer
- A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene
- Eastman Eastman AP005 Copolyester
- Fainplast Compounds GS 7303 Flexible PVC, Injection Molding for Footwear
- Ceradyne Ceralloy® 546-4E Boron Carbide
- Chang Chun Plastic PBT1200M General Purpose PBT
Copyright © lookpolymers.com All Rights Reserved