Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized |
Manufacturer | Techmer ES |
Trade Name | HiFill® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Techmer ES HiFill® PA6/6 GF33 HS L BK001 33% Glass Filled.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
Water Absorption | 1.8 % @Time 86400 sec |
1.8 % @Time 24.0 hour |
ASTM D570 |
Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 115 | 115 | ASTM D785 |
Tensile Strength, Yield | 159 MPa | 23000 psi | ASTM D638 |
Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |