- LyondellBasell Lupolen® 5261 Z Q 456 B High Density Polyethylene, Pipe and Sheet Extrusion Grade
LyondellBasell Lupolen® 5261 Z Q 456 B High Density Polyethylene, Pipe and Sheet Extrusion Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Lupolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 5261 Z Q 456 B High Density Polyethylene, Pipe and Sheet Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lupolen 5261 Z Q 456 B is a high density polyethylene (HDPE) with high melt viscosity for ram extrusion of peroxide crosslinked pipes (PE-Xa). The product is supplied as a nominal 20 mesh (840 um) powder. It is not intended for medical or pharmaceutical applications. Processing Method: Extrusion Pipe, Sheet and Semi Finished Products. Physical Form: Powder. Typical Customer Applications: Plumbing, Heating and Cooling.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D1505 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2"/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | 2"/min; ASTM D638 |
| Tensile Modulus | 1.34 GPa | 195 ksi | 1% Secant; 0.5"/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 56.7 °C | 134 °F | ASTM D3418 |
| Vicat Softening Point | 80.0 °C | 176 °F | B/50 K/h 10N; ASTM D1525 |
| 130 °C | 266 °F | A/50 K/h 10N; ASTM D1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® EFX830ME PC
- Polymer Resources NY66-IM2-[color]-H Impact Modified Nylon 66, Heat Stabilized
- Gwent Electronic Materials C2030529D3 Gold Via Ink
- Indium Corp. Indalloy 56 Bismuth Solder Alloy
- Samsung Cheil Industries Starex® VE-0558 ABS, Unreinforced FR
- UBE UBESTA® 3030U Nylon 12 (After Nitric Acid (10%) for 1000 hours)
- DuPont Performance Polymers Neoprene WHV-100 Polychloroprene Rubber
- Dow NRD6-589 Polypropylene Random Copolymer Resin
- Braskem Green PE SLL218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- Buckeye Polymers BP RPP 2012 T BLK Polypropylene, Talc Filled