Honeywell Aegisâ„¢ H100MP Nylon 6 Extrusion Grade Homopolymer Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Honeywell |
| Trade Name | Aegis™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Aegisâ„¢ H100MP Nylon 6 Extrusion Grade Homopolymer Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Aegis H100MP is a lubricated and nucleated medium viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. If conforms to Food and Drugs Administration requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermo-forming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.Applications:Processed MeatFresh Red MeatPoultryFishCheeseDried FoodChilled Fruit JuicesInformation provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Permeability | 992 g mil/ (m2 day) @Temperature 38.0 °C |
64.0 g mil/ (100 in2 day) @Temperature 100 °F |
ASTM F1249 |
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D1505 |
| Water Absorption | <= 0.80 % | <= 0.80 % | Extractable Content |
| 1.6 % | 1.6 % | in 24 hours | |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | at 50% RH |
| Water Absorption at Saturation | 9.5 % | 9.5 % | |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Viscosity Measurement | 3.35 | 3.35 | 96% SAV |
| 100 | 100 | FAV; ASTM D789 | |
| Maximum Moisture Content | 0.080 | 0.080 | |
| Melt Flow | 2.6 g/10 min @Load 1.00 kg, Temperature 235 °C |
2.6 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Molded; ASTM D882 |
| Film Tensile Strength at Yield, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 |
| Film Elongation at Break, TD | 340 % | 340 % | ASTM D882 |
| Elongation at Break | 3.8 % | 3.8 % | Molded; ASTM D882 |
| Tensile Modulus | 0.590 GPa | 85.6 ksi | TD; ASTM D882 |
| 0.700 GPa | 102 ksi | MD; ASTM D882 | |
| 3.24 GPa | 470 ksi | Molded; ASTM D882 | |
| Flexural Strength | 110 MPa | 16000 psi | Molded; ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | Molded; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | Molded; ASTM D256 |
| Tear Strength, Total | 2070 N | 465 lb (f) | Graves, TD; ASTM D1004 |
| 2140 N | 481 lb (f) | Graves, MD; ASTM D1004 | |
| Elmendorf Tear Strength MD | 89700 g | 89700 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 96900 g | 96900 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 90.0 MPa | 13100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 80.0 MPa | 11600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Cast Film |
| 246 - 254 °C | 475 - 489 °F | Tubular (Blown) Film | |
| Adapter Temperature | 260 °C | 500 °F | Tubular (Blown) Film |
| 260 - 266 °C | 500 - 511 °F | Cast Film | |
| Die Temperature | 254 °C | 490 °F | Tubular (Blown) Film |
| 260 °C | 500 °F | Cast Film | |
| Melt Temperature | 240 °C | 464 °F | Molded |
| 254 - 260 °C | 489 - 500 °F | Tubular (Blown) Film | |
| 260 - 270 °C | 500 - 518 °F | Cast Film | |
| Mold Temperature | 80.0 °C | 176 °F | Molded |
| Moisture Content | 0.040 % | 0.040 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Deflection Temperature, | 61°C | ASTM D648 |
| Puncture Index | 470 gm/mil | ASTM D1306, MD |
| Puncture Strength | 960 g | ASTM D1306, MD |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK) (Unverified Data**)
- Sekisui PIOCELAN OP-30D Moldable Polymer Foam
- Shin-Etsu Silicones FE-361TU Fluorosilicone Elastomer
- Techmer ES HiFill® PA6/6 GF55 HS L BK 55% Glass Filled
- Silberline Silvex® 430-15-C
- Samsung Cheil Industries Starex® SV-0165 U ABS, Unreinforced Extrusion Grade
- Covestro Apec® 1897 Polycarbonate
- BASF Heligoen® Green L 9361 Color Additive
- Eurotec® Tecomid® NB40 MF20 GR003 FY70 PA6, 20% mineral filled, flame retardant - halogen free (RoHS compliant), grey RAL 7035
Copyright © lookpolymers.com All Rights Reserved