Gromax BTG30-DN03N1 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTG30-DN03N1 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 113 MPa | 16400 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 3.4 % | 3.4 % | 50 mm/min; ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 5.59 GPa | 811 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.60 kJ/m² | 4.57 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.630 J/cm² @Temperature -30.0 °C |
3.00 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 1.02 J/cm² @Temperature 23.0 °C |
4.85 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 287 °C | 518 - 549 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 4669 Conductive Caulk/Sealant
- Lotte Chemical Titan TITANEX® MR4086 Medium density polyethylene resin (discontinued **)
- SGL Carbon Group SIGRAFIL C® C25 S006 APS Staple Carbon Fiber, Aromatic Polymer Sizing
- TIMCAL TIMREX® GB98/75 Natural Graphite
- ExxonMobil PP1063L1 Polypropylene Homopolymer
- ExxonMobil 22M Mobilgear SHC
- DuPont Performance Polymers Hytrel® HTR8785 BK482 Polyester Elastomer TPC-ET (Unverified Data**)
- Beijing Evergrow Resources Activated Carbon Paper
- DuPont Performance Polymers Zytel® FG7301 NC010 Nylon 6 (Unverified Data**)
- PolyOne Synprene® RT-3820M Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved