- Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content
Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-501NK Fluoroelastomer Terpolymer, Diamine Curable Grade, 68% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good mechanical characteristics.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.92 g/cc | 1.92 g/cc | at 25°C |
| Oxygen Transmission | 88.0 cc-mm/m²-24hr-atm | 224 cc-mil/100 in²-24hr-atm | |
| Nitrogen Transmission | 59.0 cc-mm/m²-24hr-atm | 150 cc-mil/100 in²-24hr-atm | |
| Carbon Dioxide Transmission | 93.0 cc-mm/m²-24hr-atm | 236 cc-mil/100 in²-24hr-atm | |
| Mooney Viscosity | 74 @Temperature 121 °C |
74 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | Peak value, at 25°C |
| Tensile Strength at Break | 17.4 MPa | 2520 psi | |
| Tensile Strength, Yield | 4.10 MPa @Strain 100 % |
595 psi @Strain 100 % |
|
| Elongation at Break | 280 % | 280 % | |
| Tear Strength | 24.5 kN/m | 140 pli | at 25°C |
| Compression Set | 30 % | 30 % | 70 hours at 25°C |
| 30 % @Temperature 175 °C |
30 % @Temperature 347 °F |
70 hours | |
| 31 % @Temperature 100 °C |
31 % @Temperature 212 °F |
70 hours | |
| 65 % @Temperature 200 °C |
65 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -16.0 °C | 3.20 °F | TR test, TR10 |
| -14.5 °C | 5.90 °F | Gehman torsion test, T10 | |
| -8.50 °C | 16.7 °F | Gehman torsion test, T2 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| Brittleness Temperature | -31.0 °C | -23.8 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 5.10 min | 0.0850 hour | Curelastmeter |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® MD PA6, Metal-detectable Nylon (ASTM Product Data Sheet)
- Mitsubishi Xantar® FC 19 R Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS - Branched
- ExxonMobil Mobil Delvac Synthetic ATF
- Plenco 5350 Phenolic, Granular, Compression Molded
- Braskem LH 218 LLDPE Cast Film Extrusion Polyethylene
- Ascend Performance Materials Vydyne® R533H01 Nylon 66, 33% Glass Reinforced, Conditioned
- EMS-Grivory Grivory® HT1V-4 HY black 9205 PA6T/6I-GF40
- Quantum Composites QC-8151C 55% Glass Fiber Vinyl Ester Static-Dissipative SMC (discontinued **)
- ExxonMobil Paxon™ AU55-003 Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved