- Fiberfil® PP-61/TC/20/UV Polypropylene Copolymer, 20% Talc, UV Stabilized
Fiberfil® PP-61/TC/20/UV Polypropylene Copolymer, 20% Talc, UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-61/TC/20/UV Polypropylene Copolymer, 20% Talc, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.012 cm/cm @Thickness 6.35 mm |
0.012 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 - 90 | 80 - 90 | ASTM D785 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Tensile Modulus | 2.14 GPa | 310 ksi | ASTM D638 |
| Flexural Strength | 37.2 MPa | 5400 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- Polycasa Design CAST PMMA
- SABIC Innovative Plastics Lexan® OQ4620 PC
- Lubrizol Advanced Materials Pearlthane® Clear 15N70 Polyether based TPU
- DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C)
- A. Schulman ComAlloy Voloy® 431 Glass/Mineral Reinforced, PET Alloy, Flame Retardant, UL
- Alliance N-40 Neodymium Iron Boron Magnetic Material
- Arkema Group KYNAR® 711 Polyvinylidene Fluoride Powder
- Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester
- Victrex® PEEK 380P Polyetheretherketone, Unreinforced
- Ineos HP50-25-153 HDPE
Copyright © lookpolymers.com All Rights Reserved