- Fiberfil® PP-60/VO/NH Polypropylene Homopolymer, Flame Retardant, non-halogenated, UL94 V0
Fiberfil® PP-60/VO/NH Polypropylene Homopolymer, Flame Retardant, non-halogenated, UL94 V0
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/VO/NH Polypropylene Homopolymer, Flame Retardant, non-halogenated, UL94 V0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.013 - 0.017 cm/cm @Thickness 3.17 mm |
0.013 - 0.017 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.018 - 0.022 cm/cm @Thickness 6.35 mm |
0.018 - 0.022 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 2.31 GPa | 335 ksi | ASTM D638 |
| Flexural Strength | 33.1 MPa | 4800 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Middle Barrel Temperature | 193 - 210 °C | 380 - 410 °F | |
| Front Barrel Temperature | 188 - 204 °C | 370 - 400 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 193 - 216 °C | 380 - 420 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- Global POM-100 High Viscosity Acetal Homopolymer
- Momentive Performance Materials AC-6028 Boron Nitride (BN) Powder
- LyondellBasell Petrothene® NA480178 Low Density Polyethylene
- Seals Eastern 7145 Fluorocarbon-Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East)
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Fainplast Compounds FAINGUM 6510 Flexible PVC, Injection Molding for Footwear
- A. Schulman ComAlloy Comtuf® 651 Nylon 6, Mineral Reinforced, Impact Modified
- Braskem TI6120Q4 High Impact Copolymer Polypropylene
- Arkema Group Orgalloy® RS 6030 Nylon 6 Alloy, 30% Glass Fiber (Conditioned)
Copyright © lookpolymers.com All Rights Reserved