Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 20.7 MPa | 3000 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable 1802-xx17FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | TM R050-36 |
Resinlab® EP1390 Medium Viscosity, Self Extinguishing Flame Retardant Epoxy Casting Resin System Resinlab™ EP1390 is a RoHS compliant, medium viscosity, self extinguishing flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Labor.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ FR PE 161 HDPE
(discontinued **) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester |
Lord Adhesives Chemglaze® V021 Polyurethane Coating Chemglaze® V-Line polyurethane coatings are moisture curing aliphatic polyurethane coatings. They are used in product finishing applications on polyvinyl-chloride (PVC) and other plastics where m.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Multibase Multi-Flamâ„¢ 2318 PP Polypropylene Features:Flame RetardantHalogen Content, Low to NoneBlooming, None Forms:PelletsProcessing Methods:Injection MoldingExtrusionCoextrusionUses:TubingPipingFurnitureInformation provided by Multibase |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Techmer ES HiFill® PA4/6 GF30 HS NAT 30% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedAppearance: Natural ColorInformation p.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Spartech PP7220 Calcium Carbonate Filled High Impact Copolymer Provides the highest level of impact of all copolymers and are useful in applications where improved processing and stiffness are required versus unfilled copolymer materials.Information provided by.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Spartech Royalstatâ„¢ R675 PS Alloy Static Control Sheet Description: Static Control SheetInformation provided by Spartech. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D412 |
Teknor Apex APEX® 3302-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D412 |
Teknor Apex Flexalloy® 3500-80 Polyvinyl Chloride Elastomer Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Features: Ultra High MWUses- Tubing, Pump PartsForms-PelletsProcessing- ExtrusionInformation provided by Te.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
Techmer ES HiFill FR® HIPS FR V-2 Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 293 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP293 is an injection molding grade olefinic thermoplastic elastomer. This product is recommended for parts requiring excellent low temperature impact properties with good dim.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524 is an injection molding grade olefinic thermoplastic elastomer. This mineral filled product is recommended for applications requiring high stiffness and low thermal exp.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene DescriptionPolypropylene PP 1188-01 is an extra high-impact polypropylene, copolymer type, with excellent low temperature properties. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristics .. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers NPP25-1111 CF15 Conductive Copolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
ExxonMobil Paxon™ 7204 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Bapolan® 6409 Polystyrene, Injection Grade Bapolan PS6409 is designed for injection molding applications requiring superior impact and gloss. It complies with US FDA21 CFR177.1640 and 94HB UL rating.Application: General purpose.Bapolene® a.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Bapolan® PS6078-G Polystyrene Compound Bapolan 6078-G is a colored, high impact polystyrene.Applications: General purpose.Bapolene® and Bapolan® are registered trademarks of Bamberger Polymers, Inc. Information provided by Bamberger Po.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 8916 Moldings & Extrusions Flexible PVC A satin finish extrusion compound best suited for extruded T-moldings, tubings and other shapes where uniform flow through the die is required. The compound exhibits excellent abrasion resistance.I.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 8941 Moldings & Extrusions Flexible PVC A clear extrusion and molding grade compound with good toughness.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 11441 Wire & Cable Flexible PVC Clear extrusion compound formulated for applications necessitating a high degree of flame retardancy.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
A. Schulman POLYTROPE™ CB 1010U-330 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope CB 1010U-330 is a color matched/color blended injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properti.. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D-638 |
Axiall 28930 Coax & Telecom Flexible PVC Non-lead stabilized 105C FT-4 riser jacket compound. UV resistant.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 20.7 MPa | 3000 psi | TM R050-36 |
Resinlab® EP1238 Black Acrylic / Epoxy Hybrid Adhesive Resinlab™ EP1238 Black is a two part acrylic / epoxy hybrid adhesive designed for bonding metals and plastics. It cures quickly at room temperature to a tough, semi-rigid material. It has good wett.. |