- Fiberfil® PP-60/FR Polypropylene Homopolymer, Flame Retardant, UL94 V0
Fiberfil® PP-60/FR Polypropylene Homopolymer, Flame Retardant, UL94 V0
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/FR Polypropylene Homopolymer, Flame Retardant, UL94 V0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm @Thickness 3.17 mm |
0.010 - 0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.012 - 0.014 cm/cm @Thickness 6.35 mm |
0.012 - 0.014 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 37.9 MPa | 5500 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 3.17 mm |
0.300 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 - 210 °C | 350 - 410 °F | |
| Middle Barrel Temperature | 193 - 227 °C | 380 - 440 °F | |
| Front Barrel Temperature | 188 - 221 °C | 370 - 430 °F | |
| Nozzle Temperature | 188 - 221 °C | 370 - 430 °F | |
| Melt Temperature | 193 - 216 °C | 380 - 420 °F | |
| Mold Temperature | 32.2 - 54.4 °C | 90.0 - 130 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound
- Albis Plastics Cellulose Acetate Propionate CP801 (UV Inhibitor Added), 12% Plasticizer (discontinued **)
- Lucite International Elvacite ® 2051 Acrylic Resin
- Schott N-K5 Glass
- Solvay Specialty Polymers Kalix® 2930 HFFR Polyamide, High Performance (HPPA), Glass Fiber
- UBE UBESTA® 3030U Nylon 12 (After Chloroform for 500 hours)
- Epoxyset Epoxibond EB-130M-1 Unfilled Epoxy Adhesive
- Axiall 9115A Wire & Cable Flexible PVC
- DuPont Performance Polymers Zytel® 70G25HSLR NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved