Polymer Property : Tensile Strength, Yield = 3600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.8 MPa	3600 psi	Type I, 51 mm/min; ASTM D638
PolyOne Maxxam™ PPC-20T Nat Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Tensile Strength, Yield	24.8 MPa	3600 psi	2 in per min, tangent; ASTM D638
Network Polymers NPP 20-3401 C/AS Description: Random Copolymer Polypropylene, Clarified, with AntistatInformation provided by Network Polymers Inc.
Tensile Strength, Yield	24.8 MPa	3600 psi	2" (50mm) per min, Type IV; ASTM D638
Formosa Plastics Formolene® HL5010 Sheet and Thermoforming HDPE (discontinued **) Extra High Molecular Weight Hexene Copolymer Formolene® HL5010 has good melt strength, excellent stress crack resistance, good rigidity, and excellent impact strength even at low temperatures. Thes..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 13% Plasticizer (discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 16% Plasticizer (discontinued **) Amorphous Cellulose Acetate Propionate (CAP)Characteristics: Strength, Hardness, Stiffness, Weatherability and Dimensional StabilityApplications: Brush Handles, Safety Glasses, Optical Products and ..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Ineos Nova ZyntarÂ® 7000 Flame Retardant Polystyrene Features:General purpose workhorse resinGood flow for injection moldingUL94 V-0 @ 1.5 mm for all colors UL94 5VA rating FOAMED @ 4.6 mm, 0.87-1.07 g/cc density, natural colorCustom colors availableA..
Tensile Strength, Yield	24.8 MPa	3600 psi	ISO 527-2/50
Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene Overview: INSPIREâ„¢ TF 8000 ES is a superior scratch and mar resistant low gloss talc filled interior grad TPO exhibiting excellent low temperature ductility, high modulus and heat performance.M..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Techmer ES HiFill FRÂ® PP FR-N X BKN001 Availability: North AmericaForms: PelletsFeatures: Flame Retardant Appearance: BlackInformation provided by TP Composites, Inc.
Tensile Strength, Yield	>= 24.8 MPa	>= 3600 psi	ASTM D638
Borealis Borstar® ME6053 Black Bimodal MD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar ME6053 is a natural, bimodal medium-density polyethylene compound produced using the Borstar process. It is characterized by its tailor made properties important in jacketing applications, ..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Total HDPE XT10B High Density Polyethylene, Pipe Resin Polyethylene: HDPE Bimodal PE4710 pipe resin (Black)Characteristics:Outstanding high temperature creep rupture strengthOutstanding slow crack growth resistanceExcellent resistance to rapid crack pr..
Tensile Strength, Yield	24.8 MPa	3600 psi	2" (50mm) per min.; ASTM D638
Formosa Plastics Formolene® 6510E Injection Molding Polypropylene Impact CopolymerApplications: General purpose injection molding of consumer products, household appliances, lawn and garden items and medical components.Formolene 6510E is a higher impact, medium st..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Total PSI 940E Impact Polystyrene Description: 940E is a super high impact polystyrene designed for high gloss sheet extrusion and thermoforming applications that require additional toughness.Applications: The combination of high gl..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Total PSI 945E Polystyrene Polystyrene 945E is a high impact polystyrene designed for applications requiring extra toughness without sacrificing mechanical properties. Excellent falling dart impact combined with the high glos..
Tensile Strength, Yield	24.8 MPa	3600 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0370 Rotational Molding Resin DescriptionSuperlinear XL 0370 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	24.8 MPa	3600 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 78A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3716 is a 12% talc filled copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	24.8 MPa	3600 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Benzoflex T-150 Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	24.8 MPa	3600 psi	Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638
Dow CONTINUUM™ DGDC-2480 NT Bimodal Polyethylene Resin CONTINUUM™ DGDA-2490 NT is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long term hydrostatic strength combined with outstanding resistan..
Tensile Strength, Yield	24.8 MPa	3600 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDB-7950 NT 7 High Density Polyethylene Resin DOW DMDB-7950 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as roll-out trash carts and other large parts with short mo..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Entec Hypro™ PPC-CC30 Natural Copolymer Polypropylene, 30% Calcium Carbonate Filled Information provided by Entec
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D-638
Axiall 8510 Moldings & Extrusions Flexible PVC A general purpose, semi-rigid T-molding and extrusion compound recommended for applications where a low gloss, matte finish is desired. The compound exhibits excellent abrasion resistance.Informati..
Tensile Strength, Yield	24.8 MPa	3600 psi	2 in/min (50 mm/min); ASTM D638
Bapolene® 3272 Polyethylene, Injection Grade Narrow molecular weight distribution injection molding resin. This high flow resin allows fast injection cycles and provides good impact strength, rigidity, and warpage resistance. This product me..
Tensile Strength, Yield	24.8 MPa	3600 psi	2 in/min (50 mm/min); ASTM D-638
Bapolene® PP5061 Polypropylene, Injection Grade Bapolene PP5061 is a PP Random Copolymer for injection molding. This resin exhibits good clarity and impact properties. This product meets FDA standards for food contact applications.Applications:..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Aclo Accucomp Polystyrene HS0600L High Impact
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Plastics Group Polifil® RP-HIPS High Impact Polystyrene Polifil® RP-High Impact Polystyrene (HIPS) combines the good stiffness properties of polystyrene, with enhanced impact properties gained by the addition of impact modifiers, usually butadiene rubbe..
Tensile Strength, Yield	24.8 MPa	3600 psi	2" (50mm) per min.; ASTM D638 Type IV
Formosa Plastics Formolene® HB4903 Sheet and Thermoforming HDPE (discontinued **) High Density Hexene CopolymerApplications: Fuel tanks, seating, garbage cans, sheet, large industrial containers.Formolene HB4903 is a high performance copolymer that is designed for the most demand..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Total PPC 4280W Polypropylene, Impact Copolymer ATOFINA 4280W polypropylene is a nucleated impact copolymer. 4280W has a low fluidity providing melt strength with excellent impact properties. It is nucleated for added stiffness and surface hard..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 13% Plasticizer (discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Albis Plastics Cellulose Acetate Butyrate B908 , 13% Plasticizer (discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Chevron Phillips HiD® 9330T HDPE Natural Pipe Resin (discontinued **) Resin Type: Gas Phase Linear Hexene CopolymerASTM D 4976 Classification: PE 235, A 54607ASTM D3350 Classification: 335540AApplications: Base resin for use in utility and conduit pipe applications.Da..