- Fiberfil® J-69/10/E High performance polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
Fiberfil® J-69/10/E High performance polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-69/10/E High performance polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 6.35 mm |
0.0060 in/in @Thickness 0.250 in |
ASTM D955 |
| 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 | |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 - 110 | 105 - 110 | ASTM D785 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ASTM D638 |
| Flexural Strength | 79.3 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 290 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 221 °C | 400 - 430 °F | |
| Middle Barrel Temperature | 216 - 232 °C | 420 - 450 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 204 - 221 °C | 400 - 430 °F | |
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi |
Users viewing this material also viewed the following:
- Network Polymers NPP 50-2753
- Pau Tai UNISTAB WP-40 Solid Complex Stabilizer
- PolyOne Elastamax™ XL-2060 Black 2001 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Meehanite AQ Flake Graphite Cast Iron
- Wellman Wellamid® GF25-66 XE-N 25% Glass Fiber Reinforced, Engineering Grade Nylon 66
- 3M RPF-C (0.24 g/cc) (Reinforced Polyurethane Foam) Continuous Strand Fiberglass
- Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, DAM
- Arlon 49090R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Bhansali Engineering Abstron IM-14S ABS Very High Rigidity Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved