Aclo Accutech ABS ABS834G40L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS834G40L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 5.299 GPa | 768.6 ksi | ASTM D638 |
| Flexural Strength | 93.01 MPa | 13490 psi | ASTM D790 |
| Flexural Modulus | 8.2985 GPa | 1203.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F |
Users viewing this material also viewed the following:
- Murtfeldt Murytal® H Acetal Homopolymer
- Polimeri Europa Riblene® MR 10 R Low Density Polyethylene - Injection Molding
- NOVA Chemicals Novapol® LM-4021-L LDPE Injection Molding Resin
- MarkeTech 95-3-2 Tungsten Alloy, AMS-T-21014 Class 3
- Haynes 230® alloy, 40% cold reduction
- Silon Tabond 2003 Adhesive Resin
- Teknor Apex Sinpolene MBW0141 Linear Low Density Polyethylene
- Lubrizol Estane® S392A Thermoplastic Polyurethane
- Hexcel® HexPly® M12 135°C Curing Epoxy Matrix
- A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT
Copyright © lookpolymers.com All Rights Reserved