Eurostar Starflam RF0057E PA66, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam RF0057E PA66, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam PF0057E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z270EM)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 0.20 %

@Temperature 23.0 °C,
Time 86400 sec
 0.20 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
Moisture Absorption 2.64 %

@Temperature 23.0 °C
 2.64 %

@Temperature 73.4 °F
 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.015 - 0.025 cm/cm

@Time 86400 sec
 0.015 - 0.025 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
 0.010 - 0.012 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
5 mm/min; ISO 527
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
Tensile Modulus 9.40 GPa
1360 ksi
1 mm/min; ISO 527
Flexural Strength 190 MPa
27600 psi
2 mm/min; ISO 178
Flexural Modulus 8.00 GPa
1160 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Hot Ball Pressure Test 240 °C

@Thickness 3.00 mm
 464 °F

@Thickness 0.118 in
 IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 ALL
140 °C

@Thickness 0.900 mm
 284 °F

@Thickness 0.0354 in
 BK
140 °C

@Thickness 0.800 mm
 284 °F

@Thickness 0.0315 in
 ALL
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 ALL
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
 ALL
140 °C

@Thickness 2.00 mm
 284 °F

@Thickness 0.0787 in
 ALL
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 ALL
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 NC
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 ALL
110 °C

@Thickness 0.900 mm
 230 °F

@Thickness 0.0354 in
 BK
110 °C

@Thickness 0.800 mm
 230 °F

@Thickness 0.0315 in
 ALL
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 ALL
110 °C

@Thickness 1.60 mm
 230 °F

@Thickness 0.0630 in
 ALL
110 °C

@Thickness 2.00 mm
 230 °F

@Thickness 0.0787 in
 ALL
110 °C

@Thickness 3.00 mm
 230 °F

@Thickness 0.118 in
 ALL
110 °C

@Thickness 1.50 mm
 230 °F

@Thickness 0.0591 in
 NC
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
 ALL
140 °C

@Thickness 0.900 mm
 284 °F

@Thickness 0.0354 in
 BK
140 °C

@Thickness 0.800 mm
 284 °F

@Thickness 0.0315 in
 ALL
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 ALL
140 °C

@Thickness 1.60 mm
 284 °F

@Thickness 0.0630 in
 ALL
140 °C

@Thickness 2.00 mm
 284 °F

@Thickness 0.0787 in
 ALL
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 ALL
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 NC
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 ALL
V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 ALL
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 ALL
V-0 - 5VB

@Thickness 3.00 mm
 V-0 - 5VB

@Thickness 0.118 in
 ALL
V-0 - 5VB

@Thickness 1.50 mm
 V-0 - 5VB

@Thickness 0.0591 in
 NC
V-0 - 5VA

@Thickness 0.900 mm
 V-0 - 5VA

@Thickness 0.0354 in
 BK
V-0 - 5VA

@Thickness 1.60 mm
 V-0 - 5VA

@Thickness 0.0630 in
 ALL
V-0 - 5VA

@Thickness 2.00 mm
 V-0 - 5VA

@Thickness 0.0787 in
 ALL
Glow Wire Test 775 °C

@Thickness 0.900 mm
 1430 °F

@Thickness 0.0354 in
 BK, Glow-Wire Ignition; IEC 60695-2-13
775 °C

@Thickness 0.400 mm
 1430 °F

@Thickness 0.0157 in
 ALL, Glow-Wire Ignition; IEC 60695-2-13
775 °C

@Thickness 0.800 mm
 1430 °F

@Thickness 0.0315 in
 ALL, Glow-Wire Ignition; IEC 60695-2-13
775 °C

@Thickness 1.50 mm
 1430 °F

@Thickness 0.0591 in
 ALL, Glow-Wire Ignition; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Dielectric Strength 16.0 kV/mm
406 kV/in
Comparative Tracking Index 600 V
600 V
PLC 0; IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.400 mm
 >= 120 sec

@Thickness 0.0157 in
 All colors; PLC 0
>= 120 sec

@Thickness 0.800 mm
 >= 120 sec

@Thickness 0.0315 in
 All colors; PLC 0
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 All colors; PLC 0
>= 120 sec

@Thickness 1.60 mm
 >= 120 sec

@Thickness 0.0630 in
 All colors; PLC 0
>= 120 sec

@Thickness 2.00 mm
 >= 120 sec

@Thickness 0.0787 in
 All colors; PLC 0
>= 120 sec

@Thickness 3.00 mm
 >= 120 sec

@Thickness 0.118 in
 All colors; PLC 0
>= 120 sec

@Thickness 0.900 mm
 >= 120 sec

@Thickness 0.0354 in
 BK; PLC 0
>= 120 sec

@Thickness 1.50 mm
 >= 120 sec

@Thickness 0.0591 in
 NC; PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.800 mm
 >= 120 arcs

@Thickness 0.0315 in
 All colors; PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 All colors; PLC 0
>= 120 arcs

@Thickness 1.60 mm
 >= 120 arcs

@Thickness 0.0630 in
 All colors; PLC 0
>= 120 arcs

@Thickness 2.00 mm
 >= 120 arcs

@Thickness 0.0787 in
 All colors; PLC 0
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 All colors; PLC 0
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 NC; PLC 0
>= 120 arcs

@Thickness 0.900 mm
 >= 120 arcs

@Thickness 0.0354 in
 BK; PLC 0
>= 120 arcs

@Thickness 0.400 mm
 >= 120 arcs

@Thickness 0.0157 in
 All colors; PLC 0